Development of Woven Fabrics with High-Count and Cooling Collagen

Volume 3 - Issue 1

Blended Yarns*, FL Huang, JY Huang and KB Cheng

  • Author Information Open or Close
    • Department of Fiber and Composite Material, Textile and Material Industrial Research Center (TMIRC), Taiwan

    *Corresponding author: Blended Yarns, Department of Fiber and Composite Material, Textile and Material Industrial Research Center (TMIRC), Taiwan

Received: December 06, 2018;   Published: December 14, 2018

DOI: 10.32474/LTTFD.2018.02.000156

Full Text PDF

To view the Full Article   Peer-reviewed Article PDF

Abstract

The 60’s cooling collagen viscose rayon blended yarn was fabricated by using ring spinning system. The blended yarn constitutions included 50wt% of regular viscose rayon with 1.5d and 38mm, 35wt% of cooling viscose rayon with 1.25d and 38mm, and 15 wt% of collagen viscose rayon fibers with 1.5d and 38mm. As mension above 60’s cooling collagen viscose rayon ring yarn was used as filling yarn. The 60’s Model Rayon(60wt%) ring yarn was used as warp yarns. The grey cloth specifications included warp density 198 ends/ 2.54cm and filling density 146 picks/2.54cm as well as the fabric width is 170cm which was produced by Picanol air-jet shuttleless loom. From the experimental results, the finished woven fabric was fabricated throuth souring, bleaching, dyeing, finishing, and heat setting processes. The color fastness of woven fabrics with high-count and cooling collagen achieved grade 4-5 according to CNS1494 testing standard.